Specificatii
COMPOZITIE CHIMICA, % DIN GREUTATE
| MARCA DE OTEL | C max | Si max | Mn max | P max | S | Ni max | V max |
|---|---|---|---|---|---|---|---|
| St52 (E 355) | 0.2 | 0.5 | 1.5 | 0.025 | 0.02-0.04 | – | – |
PROPRIETATI MECANICE (Conform cu EN 10305-1; DIN 2391)
| MARCA DE OTEL Conditii de livrare | Rm Rezistenta la rupere | Rp0.2 Limita de curgere | A5 Alungirea la rupere |
|
|---|---|---|---|---|
| – N/mm2 – | – N/mm2 – | – % min – | ||
| Grosime perete ≤ 16mm | Grosime perete ≥ 16mm | |||
| E 355 +SR | 600 | 520 | 490 | 14 |
| E 355 +N | 490-630 | 355 | 355 | 22 |
PROPRIETATI MECANICE (Conform EN 10305-2; DIN 2393)
| MARCA DE OTEL Conditii de livrare | Rm Rezistenta la rupere | Rp0.2 Limita de curgere | A5 Alungirea la rupere |
|
|---|---|---|---|---|
| – N/mm2 – | – N/mm2 – | – % min – | ||
| Grosimea peretelui ≤ 16mm | Grosimea peretelui ≥ 16mm | |||
| E 355 +C (St 52 BK) | 640 | 540 | 500 | 7 |
Rezistenta la coroziune
Conform ISO 9227:1990 pentru testele AASS, NSS si ISO 10289:1999 la evaluarea rezultatelor
| Diametru exterior (mm) | Min Rating 9 (maxim 0.1% din suprafata cu puncte de coroziune) | ||
|---|---|---|---|
| 32 to 200 | 120 h NSS | 40 h AASS | |
| ISO 9227 | ASTM | DIN 50021 | Tip ceata salina |
| NSS | B 117 | SS | Neutra |
| AASS | B 287 | ESS | Acetica |
| CASS | B 368 | CASS | Cupro-acetica accelerata |
Corespondenta marci otel
| EN 10305-1 10305-2 | DIN 2391 2393 17179 | AFNOR NF-A49310 NF-A49643 | B.S. 6323 | UNI 7945 7946 663 6403 | JIS G3445 | ASTM A 513 |
|---|---|---|---|---|---|---|
| E355 | St52 St52-3 | Tu 52b Ts 47a | CEW5-ERW5 | Fe 490 Fe 510 D Fe 52-2 Fe 510 | STKM 19 | 1024 |
| E410 | StE 460 | 20MV6 | – | – | – | – |